Catalyst for decreasing the content of nitrogen oxides in flue gases

ABSTRACT

A catalyst for decreasing the content of nitrogen oxides in flue gases. The catalyst contains at least one of the metals titanium, zirconium, vanadium, tungsten, molybdenum, or cerium in the form of one or more of their oxides combined with a silicate with a three-layer structure (three-layer silicate) which is or comprises talc. The three-layer silicate is preferably acid-activated while essentially retaining its crystalline layer structure and being not yet X-ray amorphous. The acid activation increases the BET surface area at least 15% and preferably at least 50% in terms of the BET surface area of the talc before acid activation. The atomic ratio of the silicon in the talc to the metal in the oxide is from 0.2 and 50 and preferably from 0.4 to 25.

BACKGROUND OF THE INVENTION

Field of the Invention

The invention concerns a catalyst for decreasing the content of nitrogen oxides in flue gases.

Background Information

Nitrogen oxides (NO_(x)) are generated both from the nitrogenous constituents of the fuel and from the nitrogen in the air when fossil fuels are burned. The oxides enter the atmosphere and become extremely detrimental to the environment.

It is known that nitrogen oxides can be converted into N₂ and H₂ O by NH₃ and that the reaction is fairly selective over a wide range of temperatures, meaning that, since it proceeds in the presence of a high excess of oxygen (as is usual in flue gases) without excessive loss of ammonia as the result of oxidation, only relatively small amounts of reductants are necessary. Various catalysts for reducing NO_(x) with ammonia are also known.

German AS No. 2 410 175, for example, discloses catalysts of this type that consist of oxides of vanadium molybdenum, and/or tungsten. the stoichiometry is V_(12-x-y) Mo_(x) W_(y), wherein 0≦x≦8.0≦y≦5 and 0.3≦(x+y)≦8.

Furthermore, German Patent No. 2 458 888 discloses a method of reductively decomposing nitrogen oxides in flue gases. A mixture of gases containing nitrogen oxides, molecular oxygen, and ammonia is contacted with a catalyst composition that contains (A) titanium in the form of oxides in an intimate mixture with (B) iron or vanadium in the form of oxides as its essential constituents.

The drawback to these catalysts is that the catalytically active constituents that they contain in the form of relatively expensive transition metals are exploited only to a low degree because they are not optimally distributed. Although the active constituents are extended by solid inert carriers, which does make them more economical, the dilution with inert material entails the risk of extensively decreasing their catalytic activity. Another drawback to these catalysts is that they also catalyze the SO₂ that is often contained in the flue gas into SO₃, which can lead for example to deposits of salts in the downstream equipment of the system.

German OS No. 3 438 367 also discloses a catalyst for decreasing the content of nitrogen oxide in flue gases by selective reduction. The catalyst consists of (A) 80 to 95% by weight of a catalytic oxide containing a sulfur oxide and is obtainable among other methods by heat treating an aqueous oxide compound of titanium or silicon, (B) 0 to 5% by weight of a catalytic oxide that contains vanadium oxide, and (C) 1 to 15% by weight of a catalytic oxide like tungsten oxide.

Considered essential to this catalyst is the formation of a solid acid composed of SiO₂ and TiO₂, its acidity modified by treatment with sulfuric acid or ammonium sulfate. The distribution of the solid acid is considered as representing the standard for controlling the adsorption of NH₃ at the surface of the catalyst and hence for improving its catalytic activity.

The SiO₂ is employed in the form of a silica sol. It is known that silica gels distinguished both by high BET surfaces and by high porosity can be obtained from SiO₂ sols, although the percentage of macropores is low, which has a deleterious effect on material transport and hence on catalytic activity.

German OS No. 2 748 471, finally, discloses a catalyst composition to be employed in the vapor-phase reduction of nitrogen oxides with ammonia, especially to reduce the content of nitrogen oxides in flue gases. This catalyst consists essentially of an oxide or sulfate of one of the metals copper, vanadium, chromium, molybdenum, tungsten, manganese, iron, or cerium on a shaped carrier that contains titanium oxide and a minor portion of a clay mineral with a mean particle size of 0.1 to 100 μm. Clay minerals, inter alia, of the three-layer type, can be employed. Up to 15% by weight of these clay minerals is claimed to increase only the stability of the catalyst. The additives have no significant effect on catalytic activity at these levels and larger amounts even have a negative effect in this respect. Due to their chemical composition, they also decrease the catalyst's resistance to flue gases that contain SO_(x).

SUMMARY OF THE INVENTION

It has been discovered that talc which is preferably acid-activated, will interact synergistically with other catalytic constituents to obtain catalysts of the aforesaid genus with improved activity. The latter catalysts can be employed in turn to extensively decrease the content of nitrogen oxide in flue gases, while simultaneously exploiting both the expensive oxidic constituents of the catalyst and the reductants and increasing its resistance to SO_(x).

The object of the invention is accordingly to provide a catalyst for decreasing the content of nitrogen oxides in flue gases and containing at least one of the metals titanium, zirconium, vanadium, tungsten, molybdenum, or cerium in the form of one or more of their oxides combined with a silicate with a three-layer structure (three-layer silicate).

The catalyst is characterized in that

(a) the three-layer silicate is or comprises talc;

(b) the atomic ratio of the silicon in the threelayer silicate to the metal(s) in the oxide(s) is from 0.2 and 50 and preferably from 0.4 to 25.

DETAILED DESCRIPTION OF THE INVENTION

Preferably, the talc is acid-activated while partly retaining its crystalline layer structure, but is not X-ray-amorphous, and the acid-activation increases the BET surface at least 15% and preferably at least 50% as compared to the BET surface of the talc before acid activation. The acid activation increases the catalytic activity and the SO_(x) stability of the catalysts.

Acid activation of the talc most like leads to the silicate layers being attacked from the edges and the ions being released from the octahedral layers. The remaining SiO₄ tetrahedral bands have a certain wedge action and steric hindrance, especially during drying, that disorients the layers, although the crystalline layer structure is essentially maintained. The result is a state intermediate between the crystalline structure of the original talc and the completely destroyed crystalline structure of amorphous silicic acid.

Acid activation increases the specific surface area which is generally determined by the BET method. An appropriately high specific surface area remains even after the acid-activated talc has been intimately mixed with the oxidic constituents of the catalyst, even when large amounts of them have been employed. Acid activation must not on the other hand be continued until only amorphous silicic acid remains because the synergistic interaction with the oxidic constituents of the catalyst will obviously cease at that point, as will be evident from a steep drop in catalytic activity at an increased content of silicic acid.

The acid-activated talc enters into synergistic interaction with the metal oxides. Although no unambiguous mechanistic explanation of this synergism can be provided at the present, reorientation of the silicate layer structure by the acid activation would seem to be a prerequisite. Conversion with, for instance, a silica gel with a similar BET surface instead of the acid-activated silicate in accordance with the invention in conjunction with the oxidic metal constituents will result in a definitely lower catalytic activity.

The specific surface area of the preferred acidactivated talc employed in accordance with the invention is preferably between about 5 and 100 m² /g.

The acidic decomposition is carried out until the SiO₂ content of the acid-activated talc is at least 2% and preferably at least 5% higher than that of the starting material. Depending on the starting material, the SiO₂ content will then be 50 to 90% by weight. Acidic decomposition is, however, not continued until only X-ray amorphous SiO₂ remains. It is discontinued at a specific degree of crystallinity on the part of the acid-activated three-layer silicate i.e. when no more than 45% extractable silicate is present. The percentage of extractable silicate is determined by washing and drying the filter cake obtained in carrying out the acidic decomposition and treating it with a soda solution as described by Y. Otsubo, Jap. J. Chem., 72, 573 (1951).

Macropores with a diameter of more than 80 nm will preferably account for at least 25% of the total volume of pores. Pore volume is determined by mercury porosimetry.

The starting materials that contain the talc can be acid activated in a way that is in itself known, preferably with aqueous mineral acids like hydrochloric or sulfuric acid. Organic acids like formic and acetic acid can, however, also be employed. The acid is employed in a concentration of from 1 to 60% by weight in terms of the solids content and preferably in the range of 10 to 40% by weight. Preliminary wet classification of the raw material can be practical. The acid-treated composition is washed with, if necessary, acidified water and filtered out.

The catalysts in accordance with the invention are also outstanding in their resistance to sulfur oxides and sulfuric acid as dictated by acid activation of talc. It has been confirmed that catalysts prepared with untreated or H-ion substituted starting silicates are especially sensitive to sulfur oxides or sulfuric acid, leading to mechanical destruction and premature aging of the catalyst.

Although, on the other hand, catalysts manufactured with amorphous silicic acid are resistant to sulfur oxides and sulfuric acid, their NO_(x) activity is definitely poor.

The starting compounds employed for the metal-oxide constituents of the catalyst in accordance with the invention are on the one hand the corresponding metal oxides and on the other the substances that can be converted into the metal oxides, e.g. the metals and hydroxides and especially salts, complex compounds, and/or oxygen acids or salts derived from the last. They can be employed if necessary in conjunction with an additive that functions as a reductant and/or complexing agent.

Cerium can for example be employed in the form of Ce₂ O₃, CeO₂, Ce(SO₄)₂, and Ce₂ (C₂ O₄)₃. Appropriate starting materials for zirconium oxide are, in addition to the oxide hydrates, for example, the zirconium and zirconyl salts like Zr(SO₄)₂, ZrCl₄, ZrOCl₂, and Zr(C₂ O₄)₂.

Appropriate starting substances for the tungsten constitutents are, for example, tungsten oxides like WO₃, W₁₀ O₂₉, W₄ O₁₁, and WO₂ and mono- and polytungstic acids, heteropolyacids, tungstates, and tungstic halides and oxyhalides. Molybdenum compounds can also be employed instead of the analogous tungsten compounds.

Appropriate vanadium starting compounds include V₂ O₅, VO₂, V₂ O₃, and VO along with ortho- and polyvanadic acids or vanadates, vanadium halides and oxyhalides like VOCl₃, for example, and various vanadium or vanadyl salts.

Appropriate titanium compounds are, in addition to the oxides and oxide hydrates, the titanium and titanyl salts, especially the halides and sulfates. Although titanyl sulfate is preferable from the economic point of view, metal-organic compounds like titanates, isopropyl titanate for example, can also be employed.

It has been discovered that expecially practical results can be achieved when the metal oxides are individually present in the following ranges of concentration (by weight):

    ______________________________________                                         TiO.sub.2 =      10-80      Gew. %                                             WO.sub.3 and/or MoO.sub.3 =                                                                     1-25       Gew. %                                             V.sub.2 O.sub.5 =                                                                               0,1-25     Gew. %                                             CeO.sub.2 =      1-25       Gew. %                                             ______________________________________                                    

with the talc accounting for the rest of the active constituents.

The metal oxides are present in the preferred catalysts in a binary, especially ternary combination.

When present in a ternary combination, the metal oxides are present in a preferred catalyst in one of the following percentages by weight:

    ______________________________________                                         (a)     (TiO.sub.2 + WO.sub.3 and/or MoO.sub.3 + V.sub.2 O.sub.5)                                             = 10-80                                         (b)     (TiO.sub.2 + CeO.sub.2 + V.sub.2 O.sub.5)                                                             = 10-80                                         (c)     (TiO.sub.2 + ZrO.sub.2 + V.sub.2 O.sub.5)                                                             = 10-80                                         (d)     (WO.sub.3 and/or MoO.sub.3 + CeO.sub.2 + V.sub.2 O.sub.5)                                             = 10-25                                         (e)     (WO.sub.3 and/or MoO.sub.3 + ZrO.sub.2 + V.sub.2 O.sub.5)                                             = 10-25                                         ______________________________________                                    

with the talc accounting for the rest of the active constituents.

The ratios between the weights of the metal oxides present in a ternary combination in a preferred catalyst are as follows:

    ______________________________________                                         (a)    WO.sub.3 and/or MoO.sub.3 :TiO.sub.2 =                                                           0.01-0.25                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                             (b)    CeO.sub.2 :TiO.sub.2 =                                                                           0.05-0.23                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                             (c)    ZrO.sub.2 :TiO.sub.2 =                                                                           0.01-0.24                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                             (d)    CeO.sub.2 :WO.sub.3 and/or MoO.sub.3 =                                                           0.1-5.0                                                      V.sub.2 O.sub.5 :WO.sub.3 and/or MoO.sub.3 =                                                     0.1-2.5                                               (e)    V.sub.2 O.sub.5 :WO.sub.3 and/or MoO.sub.3 =                                                     0.1-2.5                                                      ZrO.sub. 2 :WO.sub.3 and/or MoO.sub.3 =                                                          0.1-10                                                ______________________________________                                    

The catalyst in accordance with the invention can be obtained, for example, by impregnating the talc with a solution containing one or more of the aforesaid metals in the form of salts and/or complex compounds and calcining it.

In another variant, the catalyst can be obtained by mechanically mixing the talc with an oxide or salt of one or more of the aforesaid metals (by grindind in a ball mill for example), impregnating the mixture, if necessary, with a solution containing one or more of the aforesaid metals in the form of salts and/or complex compounds, and calcining it.

The catalysts in accordance with the invention can also be obtained by precipitating or reprecipitating at least one compound containing one or more of the aforesaid metals in the presence of a suspension of the talc washing out the foreign ions, and calcining.

The compound or compounds containing one or more of the aforesaid metals can also be precipitated or reprecipitated in the presence of a mixture of suspensions of the talc and of an oxide or salt of one or more of the aforesaid metals. This stage is followed by washing out the foreign ions and calcining.

The result of these procedures is an almost optimally intimate mixture of the oxidic metal constituents with the acid-activated three-layer silicate.

If the oxidic metal constituents consist of several metal oxides, the particular starting compounds can either be precipitated together or one after another in several stages, with the sequence of precipitation stages generally affecting the catalytic activity and needing to be optimized individually. It can of course turn out to be practical to impregnate the talc, subsequent to one or more precipitaton stages, if necesssary, with a solution of a corresponding transition compound. Impregation can occur either before or after shaping and calcining the catalyst.

The catalyst in accordance with the invention can also contain an inert carrier. The catalyst is usually present in the from of molded shapes, expecially balls, tablets, extruded shapes, oblong or flat honeycombs, (called "channel grids") plates, rods, tubes, rings, wagon wheels, or saddles.

The shapes can be obtained for example by tableting or extruding the catalyst composition, with additives also mixed in, if necessary, to facilitate shaping. Such additives include, for example, graphite and aluminum stearate. Additives to improve the surface structure can also be mixed in. These include, for example, organic substances that will burn up and leave a porous structure during the subsequent calcination.

It is not absolutely necessary to employ additives to facilitate shaping because the starting material is plastically deformable even when intimately mixed with the metal constituents. Neutral bentonites or other binders like kaolin or cement can, however, also be added. The material is generally shaped with water or organic solvents like monovalent or polyvalent alcohols added.

The catalysts in accordance with the invention are usually dried after being shaped, and calcined at temperatures of 200° C. to 700° C. and preferably 300° C. to 550° C. Inorganic fibrous materials can also be added before shaping to improve strength. Calcination activates the catalyst, which accordingly obtains its practical properties, expecially if the aforesaid temperature ranges are maintained.

The examples hereinbelow specify typical procedures for manufacturing the catalysts in accordance with the invention.

Another object of the invention is the use of the catalysts in accordance with the invention for reductively decreasing the content of nitrogen oxide in flue gases that contain, in addition to the usual constituents, sulfur oxides (SO_(x)), whereby NH₃ is employed as a reductant.

In reducing with NH₃, the content of nitrogen oxides in the flue gases is decreased due to the formation of N₂ and H₂ O. Although nitrogen oxides (NO_(x)) are any compound of nitrogen and oxygen like NO, N₂ O₃, NO₂, and N₂ O₅, the most important in the present context are NO and NO₂, mainly the former.

The concentration of NO_(x) in the flue gases that are to be cleaned can vary widely, generally ranging from 100 ppm by volume to 5% by volume. The molar ratio of NH₃ to NO_(x) is generally 0.3 to 3, preferably 0.6 to 1.5, and can be regulated by controls technology to obtain maximum NO_(x) conversion at the minimum possible NH₃ slippage. The NH₃ can be added either in the form of a gas or in aqueous solution.

The catalysts in accordance with the invention are distinguished beyond known catalysts by a very extensively selective conversion of the ammonia that is preferred for reducing the nitrogen oxides. In conventional methods, expecially at high operating temperatures, a considerable amount of the ammonia does not get consumed during the desired NO_(x) removal, but oxidizes due to the oxygen present in the flue gas. This leads to additional nitrogen formation or decreases the conversion of NO_(x) observed between the entrance into and exit from the reactor, leading to unnecessary consumption of NH₃.

Any of the reactors employed for heterogeneous catalyzed gas-phase reactions are appropriate for the NO_(x) reduction if their design allows high volumetric flue-gas currents in relation to output. Permissible space velocities are in the range of 500 to 20,000 and preferably 1000 and 15,000 liters of gas per hour and liters of catalyst in terms of a gas to 0° C and 1 bar. Space velocity will be designated as the dimension h⁻¹ in what follows for the sake of simplicity. Appropriate reaction temperatures range from approximately 200° C to 600° C and preferably 250° to 430° C. If the temperatures are much higher the ammonia can be oxidized by the oxygen in the flue gas, removing the ammonia from the reaction along with the nitrogen oxides and allowing the degree of NO_(x) reduction to drop. This undesirable effect, however, is not as powerful with the catalysts in accordance with the invention as with known catalysts.

Typical examples of the manufacture and use of the catalysts in accordance with the invention will now be specified.

The effectiveness of the catalysts with respect to eliminating nitrogen oxides from mixtures of gases that contain, among other substances, oxygen and sulfur oxides is determined by contacting the catalyst with a stream of gas flowing through a tube packed with the catalyst and electrically heated from outside. The mixture of gases is composed of:

    ______________________________________                                         O.sub.2   3%         by volume                                                 H.sub.2 O 10%        by volume                                                 NO        750        ppm by volume                                             NO.sub.2  50         ppm by volume                                             NH.sub.3  800        ppm by volume                                             SO.sub.2  950        ppm by volume                                             SO.sub.3  50         ppm by volume and                                         N.sub.2   to make up 100% by volume.                                           ______________________________________                                    

The concentration of NO_(x) in the mixture was measured before and after it traveled through the catalyst packing by an appropriated analyzer (chemoluminescence). The level of NO_(x) converted subsequent to establishment of a stationary state and as defined by the equation ##EQU1## was selected as the measure for the effectiveness of the catalysts in reducing the nitrogen oxides. c_(NO).sbsb.x represents the concentrations of NO and NO₂, and the superscripts E and A the state of the mixture of gases before and after traveling through the catalyst.

EXAMPLE 1

(a) 2 kg of talc with a BET surface area of 5 m² /g, and the chemical composition listed in Table I, are stirred into 8 liters of an aqueous solution of HCl for 6 hours at 80° C. The HCl level is about 20% by weight of the dry substance. The material is suctioned off and the filter cake thoroghly washed with acidified water (pH adjusted to 3.5 with HCl). The resulting acid-activated talc ("AAT" hereinafter) after drying at 200° has a BET surface area of 33 m² /g. Its chemical composition is also listed in Table I.

(b) 180 g TiOSO₄ is stirred into a suspension of 400 g AAT obtained in step (a). The batch is neutralized with ammonia. The solids are suctioned-off, washed free of sulfates, dried for 15 hours at 120° C., and kneaded into a solution of tungstic acid (9.7 g) in ammonia and into a solution obtained by reducing ammonium metavanadate (1.3 g) with a 1.6-fold excess of oxalic-acid dihydrate. The amounts of solvents were selected to ensure easy-to-knead pastes. The percentage of the pore volume occupied by macropores with a diameter larger than 80 nm as determined by Hg porosimetry was 77.1%.

EXAMPLE 2

400 g of the talc used as starting material in Example 1 are charged with titanyl sulfate, ammoniacal tungstic acid solution and ammonium metavanadate, following the procedure of Example 1, step (b).

The composition of the catalysts, the reaction temperatures and the NO_(x) conversions at a space velocity of 6400 h⁻¹ are listed in Table II. The above-mentioned gas mixture was used for carrying out the reactions; the NO_(x) conversions were calculated according to the above-mentioned formula.

                                      TABLE I                                      __________________________________________________________________________     Composition of the silicates                                                                 SiO.sub.2                                                                         Al.sub.2 O.sub.3                                                                   Fe.sub.2 O.sub.3                                                                   CaO                                                                               MgO                                                                               Na.sub.2 O                                                                         K.sub.2 O                                                                         Ignition                                 Silicate      (%)                                                                               (%) (%) (%)                                                                               (%)                                                                               (%) (%)                                                                               loss (%)                                 __________________________________________________________________________     Crude talc from Example 1                                                                    47.2                                                                              11.3                                                                               1.9 0.5                                                                               28.3                                                                              0.2 0.5                                                                               9.1                                      AAT* from Example 2                                                                          55.4                                                                               9.3                                                                               1.4 0.2                                                                               24.9                                                                              0.2 0.5                                                                               7.5                                      __________________________________________________________________________      *Acid-activated talc                                                     

                                      TABLE II                                     __________________________________________________________________________     Composition of the catalysts and NO.sub.x conversions                                            V.sub.2 O.sub.5                                                                    WO.sub.3                                                                          TiO.sub.2                                                                         NO.sub.x conversion (%)                            Example                                                                             Silicate constituent                                                                     (%)                                                                               (%) (%)                                                                               (%)                                                                               250° C.                                                                      300° C.                                                                     350° C.                                                                     400° C.                        __________________________________________________________________________     1    Acid-activated talc                                                                      80 0.2 1.8                                                                               18 42   93  98  98                                    2    Crude talc                                                                               80 0.2 1.8                                                                               18 not detd.                                                                           76  90  91                                    __________________________________________________________________________ 

What is claimed is:
 1. A catalyst for decreasing the content of nitrogen oxides in flue gases comprising at least one metal selected from the group consisting of titanium, zirconium, vanadium, tungsten, molybdenum and cerium in the form of one or more of their oxides and a three-layer silicate comprising talc, the atomic ratio of the silicon in the talc to the metal in the oxide being between 0.2 50, wherein said talc is acid-activated, while partly retaining its crystalline layer structure, and being not yet X-ray amorphous, the acid activation increasing the BET surface area at least 15% in terms of the BET surface area of the talc before acid activation.
 2. A catalyst according to claim 1, wherein the increase of the BET surface area is at least 50% of the BET surface area of the three-layer silicate before acid activation.
 3. A catalyst according to claim 1, wherein the atomic ration of the silicon in the three-layer silicate to the metal in the oxide is from 0.4 to
 25. 4. A catalyst according to claim 1, wherein the SiO₂ content of the three-layer silicate is at least 2% higher than that of the starting material.
 5. A catalyst according to claim 1, wherein the SiO₂ content of the three-layer silicate is at least 5% higher than that of the starting material.
 6. A catalyst according to claim 1, wherein macropores with a diameter of more than 80 nm account for at least 25% of the total volume of pores of the catalyst.
 7. A catalyst according to claim 1, wherein the metal oxides are individually present in the following ranges of concentration:

    ______________________________________                                         TiO.sub.2 :        10-80% by weight,                                           WO.sub.3 and/or MoO.sub.3 :                                                                        1-25% by weight,                                           V.sub.2 O.sub.5 : 0.1-25% by weight, and                                       CeO.sub.2 :         1-25% by weight,                                           ______________________________________                                          with the acid-activated three-layer silicate accounting for the rest of      the active constituents.


8. A catalyst according to claim 1, wherein when present in a ternary combination, the metal oxides are present in one of the following percentages by weight:

    ______________________________________                                         (a)    (TiO.sub.2 + WO.sub.3 + and/or MoO.sub.3 + V.sub.2 O.sub.5)                                            = 10-80                                         (b)    (TiO.sub.2 + CeO.sub.2 + V.sub.2 O.sub.5)                                                              = 10-80                                         (c)    (TiO.sub.2 + ZrO.sub.2 + V.sub.2 O.sub.5)                                                              = 10-80                                         (d)    (WO.sub.3 and/or MoO.sub.3 + CeO.sub.2 + V.sub.2 O.sub.5)                                              = 10-25                                         (e)    (WO.sub.3 and/or MoO.sub.3 + ZrO.sub.2 + V.sub.2 O.sub.5)                                              = 10-25                                         ______________________________________                                          with the acid-activated three-layer silicate accounting for the rest of      the actve constituents.


9. A catalyst according to claim 8, wherein the ratios between the weights of the metal oxides present in the ternary combination are

    ______________________________________                                         (a)   WO.sub.3 and/or MoO.sub.3 :TiO.sub.2 =                                                           0.01-0.25                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                              (b)   CeO.sub.2 :TiO.sub.2 =                                                                           0.05-0.23                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                              (c)   ZrO.sub.2 :TiO.sub.2 =                                                                           0.01-0.24                                                    V.sub.2 O.sub.5 :TiO.sub.2 =                                                                     0.01-0.11                                              (d)   CeO.sub.2 :WO.sub.3 and/or MoO.sub.3 =                                                           0.1-5.0                                                      V.sub.2 O.sub.5 :WO.sub.3 =                                                                        0.1-2.5 and                                          (e)   V.sub.2 O.sub.5 :WO.sub.3 and/or MoO.sub.3 =                                                     0.1-2.5                                                      ZrO.sub.2 :WO.sub.3 =                                                                            0.1-10                                                 ______________________________________                                    


10. A catalyst according to claim 1, wherein the catalyst is in the form of shaped bodies, oblong or flat honeycomb, plates, rods, tubes, rings, wagon wheels or saddles.
 11. A catalyst according to claim 1, wherein the catalyst is produced by impregnating the three-layer silicate with a solution containing one or more of the metals in the form of salts and/or complex compounds and conducting calcination.
 12. A catalyst according to claim 1, wherein the catalyst is produced by mechanically mixing the three-layer silicate with an oxide or salt of one or more of the metals, impregnating the resultant mixture with a solution containing one or more of the metals in the form of salts and/or comples compounds, and conducting calcination.
 13. A catalyst according to claim 1, wherein the catalyst is produced by precipitating or reprecipitating at least one compound containing one or more of the metals in the presence of a suspension of the three-layer silicate, washing out the foreign ions, and calcining.
 14. A catalyst according to claim 1, wherein the catalyst is produced by precipitating or reprecipitating at least one compound containing one or more of the metals in the presence of a mixture of suspensions of the three-layer silicate and of an oxide or salt of one or more of the metals, washing out the foreign ions, and calcining. 